RESEARCH ON REUSING WASTE PLASTIC FLAKES OF SCRAP PLASTIC GRINDING FACILITIES TO PRODUCE CONCRETE BRICKS ; NGHIÊN CỨU TÁI SỬ DỤNG VỤN NHỰA THẢI CỦA CÁC HỘ XAY NHỰA PHẾ LIỆU ĐỂ SẢN XUẤT GẠCH KHÔNG NUNG

This study focuses on assessing the possibility of using plastic flakes from scrap plastic grinding facilities of Trieu Khuc plastic recycling village to produce concrete bricks. The study also tests the addition of denatured aluminum slag into brick to minimize the amount of solid waste that would be buried. These brick samples are composed of dust mites, cement, waste plastic flakes and/or denatured aluminum slag. The test results of concrete brick samples show that the percentage of waste plastic chips, denatured aluminum slag can reach 25-35% of the mixing volume. The compressive strength of the test samples can reach the grade of M35 bricks, even close to the grade of M100 bricks. The addition of denatured aluminum slag requires further research as well as additional consideration of adding a binding additive to increase the compressive strength of the product brick. ; Nghiên cứu này tập trung vào đánh giá khả năng sử dụng vụn nhựa thải từ các hộ xay nhựa phế liệu của làng nghề tái chế nhựa Triều Khúc để sản xuất gạch không nung. Nghiên cứu cũng tiến hành thử nghiệm bổ sung xỉ nhôm biến tính trong thành phần gạch nhằm giảm thiểu lượng chất thải rắn đem đi chôn lấp. Các mẫu gạch cấp phối có thành phần là đá mạt, xi măng, vụn nhựa thải và hoặc bã xỉ nhôm biến tính. Kết quả kiểm tra các mẫu gạch không nung cho thấy tỷ lệ vụn nhựa thải, xỉ nhôm biến tính có thể đạt 25 - 35% thể tích phối liệu. Cường độ chịu nén với các mẫu thử nghiệm có thể đạt mác gạch M35, thậm chí là gần đạt mác gạch M100. Việc bổ sung thêm xỉ nhôm biến tính cần phải nghiên cứu thêm cũng như xem xét bổ sung thêm phụ gia kết dính để gia tăng cường độ chịu nén của gạch sản phẩm.