Mechanical attrition of lanthanum hydroxide with hydrogen gas followed by sintering.

In Indonesia, the use of monazite has been carried out for the rare earth processing industry by PT. Timah (Persero) Tbk with raw material in the form of tin mining waste. The pilot plant produces rare earth metal products in the form of hydroxides, such as lanthanum hydroxide La(OH) 3 , with a price range of US$ 230 per kg. Application of La(OH) 3 includes water treatment, specialty glass, catalyst, optical coating, gas-exhaust convector, hydrogen storage material, superconductor, and dielectric material. This research was intended to specifically ball-mill lanthanum hydroxide (La(OH) 3 ) with hydrogen gas followed by sintering and to characterize the product materials. The expected yield of this synthesis was material for the superconducting application. The sintering temperature was pre-determined based on a differential scanning calorimeter (DSC) test, which was 550°C for 1 hour. The product characterization included x-ray diffraction (XRD), particle size analysis (PSA), and scanning electron microscopy (SEM). Lanthanum di-hydride (LaH 2 ) and lanthanum oxide (La 2 O 3 ) were obtained as the products of this ball-milling, with the final compositions of 91.1 wt.% and 8.9 wt.%, respectively. The average particle size of the LaH 2 and La 2 O 3 powder mixture was 190.3 nm, downsized from 323.7 nm of La(OH) 3 through the ball-milling process. SEM observation for the ball-milling product before sintering indicated the presence of particle aggregations. The increase in La 2 O 3 content after sintering induced a higher crystallite strain of 2.0±0.1% compared to that after ball-milling. [ABSTRACT FROM AUTHOR]

Copyright of AIP Conference Proceedings is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)