Structural, thermal and magnetic properties of orthoferrite holmium nanoparticles synthesized by a simple co-precipitation method.

In this study, holmium orthoferrite (o-HoFeO 3 ) nanoparticles were successfully synthesized by simple co-precipitation method without adding gelling organic polymers. Structures, morphologies, elemental composition, thermal, and magnetic properties of the product were characterized by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDX), thermogravimetry and differential scanning calorimetry (TG-DSC), and vibrating sample magnetometer (VSM). After annealing the precursors at different temperatures for 60 min, nanocrystrals with orthorhombic perovskite structure were obtained. Crystallite size (D PXRD = 22.13–53.74 nm), particle size (D TEM/SEM = 20–60 nm), and lattice volume (V = 223.65–224.99 Å 3 ) increased with the annealing temperature. The optimal annealing temperature for obtaining the single crystalline phase of o-HoFeO 3 was ≥ 750 °C, and the o-HoFeO 3 crystalline phase remained stable at temperatures ≥ 1050 °C. The synthesized o-HoFeO 3 nanoparticles exhibited a uniform spherical shape, with a size of 20–60 nm, and exhibited the properties of a paramagnetic material at 300 K. Notably, the coercive force and residual magnetism of the synthesized material were much smaller than those reported in previous studies for similar materials. The experimental results in this work may provide fundamental support to the research and development of magnetic material. [ABSTRACT FROM AUTHOR]

Copyright of Journal of Materials Science: Materials in Electronics is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)